رشد بریجمن تک کریستال CdWO4
مقاله انگلیسی تحت عنوان Bridgman growth of CdWO4 single crystals
دارای 4 صفحه انگلیسی
ترجمه فارسی آن دارای 7 صفحه و 1800کلمه
چکیده انگلیسی:
The growth of large size CdWO4 single crystals by vertical Bridgman process is reported in this letter. CdWO4 polycrystalline material with stoichiometric composition was synthesized from CdO and WO3 as the initial materials by solid-state reaction. In the Bridgman growth, the platinum crucibles charged with material were sealed so as to avoid the harmful volatilization of the melt. By means of the growing parameters such as a crucible lowering rate of 0.5–1.5 mm/h and a temperature gradient around 30–40 1C/cm across the solid–liquid interface under a furnace temperature of 1350–1400 1C, a transparent CdWO4 crystal as large as +4070mm has been grown by the vertical Bridgman process successfully. The crystal was characterized by X-ray diffraction (XRD), optical transmittance, X-ray stimulated luminescence spectrum. The desirable crystalline quality of the grown crystals is verified by XRD rocking curve. The crystal shows a high optical transmittance in the visible wavelength range and a strong emission peaked at 470nm under X-ray excitation.
ترجمه فارسی:
در این مقاله رشد تک کریستال بزرگ CdWO4 به روش بریجمن عمودی گزارش شده است. ماده ی پلی کریستالی CdWO4 با ترکیب استوکیومتری از واکنش حالت جامد مواد اولیه ی CdO و WO3 تولید شد. در رشد بریجمن، بوته های پلاتینی شارژ شده، آب بندی می شوند تا از تبخیر ناخواسته ی مذاب جلوگیری گردد. با به کارگیری پارامترهای رشد اعم از نرخ پایین آوردن بوته mm/h 5/0- 5/1 و گرادیان دمایی ℃/cm 30- 40 در فصل مشترک مایع- جامد، کریستال CdWO4 شفاف با ابعاد mm 40×70 در کوره ای با دمای ℃ 1350- 1400 و به روش بریجمن عمودی تشکیل می شود. کریستال حاصل با استفاده از روش های XRD، عبور نور و طیف لومینسانس شبیه سازی شده با اشعه ی X مشخص یابی گردید. کیفیت مطلوب کریستال نیز از طریق منحنی های صخره ای XRD ارزشیابی شد. این کریستال در محدوده ی طول موج مرئی، عبور نور زیادی نشان داد و در اثر تهییج با اشعه ی X، پیک شدیدی را در nm 470 گسیل کرد.
دانلود رایگان مقاله انگلیسی
دانلود مقاله دات کام 
توضیحات محصول
رشد بریجمن تک کریستال CdWO4
مقاله انگلیسی تحت عنوان Bridgman growth of CdWO4 single crystals
دارای 4 صفحه انگلیسی
ترجمه فارسی آن دارای 7 صفحه و 1800کلمه
چکیده انگلیسی:
The growth of large size CdWO4 single crystals by vertical Bridgman process is reported in this letter. CdWO4 polycrystalline material with stoichiometric composition was synthesized from CdO and WO3 as the initial materials by solid-state reaction. In the Bridgman growth, the platinum crucibles charged with material were sealed so as to avoid the harmful volatilization of the melt. By means of the growing parameters such as a crucible lowering rate of 0.5–1.5 mm/h and a temperature gradient around 30–40 1C/cm across the solid–liquid interface under a furnace temperature of 1350–1400 1C, a transparent CdWO4 crystal as large as +4070mm has been grown by the vertical Bridgman process successfully. The crystal was characterized by X-ray diffraction (XRD), optical transmittance, X-ray stimulated luminescence spectrum. The desirable crystalline quality of the grown crystals is verified by XRD rocking curve. The crystal shows a high optical transmittance in the visible wavelength range and a strong emission peaked at 470nm under X-ray excitation.
ترجمه فارسی:
در این مقاله رشد تک کریستال بزرگ CdWO4 به روش بریجمن عمودی گزارش شده است. ماده ی پلی کریستالی CdWO4 با ترکیب استوکیومتری از واکنش حالت جامد مواد اولیه ی CdO و WO3 تولید شد. در رشد بریجمن، بوته های پلاتینی شارژ شده، آب بندی می شوند تا از تبخیر ناخواسته ی مذاب جلوگیری گردد. با به کارگیری پارامترهای رشد اعم از نرخ پایین آوردن بوته mm/h 5/0- 5/1 و گرادیان دمایی ℃/cm 30- 40 در فصل مشترک مایع- جامد، کریستال CdWO4 شفاف با ابعاد mm 40×70 در کوره ای با دمای ℃ 1350- 1400 و به روش بریجمن عمودی تشکیل می شود. کریستال حاصل با استفاده از روش های XRD، عبور نور و طیف لومینسانس شبیه سازی شده با اشعه ی X مشخص یابی گردید. کیفیت مطلوب کریستال نیز از طریق منحنی های صخره ای XRD ارزشیابی شد. این کریستال در محدوده ی طول موج مرئی، عبور نور زیادی نشان داد و در اثر تهییج با اشعه ی X، پیک شدیدی را در nm 470 گسیل کرد.
دانلود رایگان مقاله انگلیسی