مدل شکست و مدل ماده ی ایزوتروپ عرضی مبتنی بر ثوابت برای پلیمرهای تقویت شده با الیاف
فایل انگلیسی 26 صفحه
فایل ترجمه فارسی 21 صفحه تعداد کلمات فایل ترجمه شده: 5800 کلمه
چکیده انگلیسی:
In this article, a constitutive formulation of a transversely-isotropic material and failure model for fiber-reinforced polymers is presented comprisin pre-failure material nonlinearities, a novel invariant based quadratic failure criterion (IQC) as well as post failure material softening. The failure surface of the IQ criterion is assumed to take the influence of triaxiality on fracture into account. Further, a distinction between fiber failure and inter-fiber failure is conducted. Material softening is governed by a fracture energy formulation and the introduction of an internal length. The constitutive model is implemented into a programming user interface of the commercial finite element program Abaqus. As results, different laminate lay-ups are modelled and exposed to different stress states in an FE analysis. The obtained failure surfaces and stress strain curves for each laminate lay-up are compared to experimental data. As further applications of the material model presented, a curved composite beam, showing delamination, and a 0°/90°/0°-rod, showing the characteristic damage state in the 90°layer, are simulated and compared.to tests
ترجمه چکیده:
در این مقاله، فرمول سازنده ماده ی ایزوتروپ عرضی و مدل شکست پلیمرهای تقویت شده با الیاف ارائه شده است که شامل غیرخطی بودن پیش از شکست ماده، معیار شکست درجه دوم بر اساس ثوابت (IQC) و نرم شدگی پس از شکست هستند. فرض می شود که سطح شکست در معیار IQ تحت تأثیر سه محوری بودن شکست قرار می گیرد. علاوه بر این، در رابطه با تمایز بین شکست الیاف و شکست بین الیاف نیز بحث خواهد شد. نرم شدن ماده توسط فرمول انرژی شکست و معرفی طول داخلی شرح داده می شود. مدل سازنده در برنامه ی المان محدود آباکوس اجرا می گردد. در نتیجه، لایه های فشرده شده پس از مدلسازی، تحت حالت های تنش مختلف در آنالیز FE قرار می گیرد. سطوح شکست حاصل و منحنی های تنش- کرنش هر لایه با داده های تجربی مقایسه می شود. به عنوان معرفی یکی از کاربردهای مدل پیشنهادی، یک تیر کامپوزیتی خمیده که تحت ورقه ای شدن قرار گرفته و یک میله ی ֯0/ ֯90/ ֯0 که خسارت وارد به آن در لایه ی ֯90 بوده است، شبیه سازی شده و از نظر نتایج تست مقایسه شدند.
فایل انگلیسی شامل 26 صفحه و فایل ترجمه فارسی شامل 21 صفحه است.
تعداد کلمات فایل ترجمه شده: 5800 کلمه
دانلود رایگان مقاله انگلیسی
دانلود مقاله دات کام 
توضیحات محصول
مدل شکست و مدل ماده ی ایزوتروپ عرضی مبتنی بر ثوابت برای پلیمرهای تقویت شده با الیاف
فایل انگلیسی 26 صفحه
فایل ترجمه فارسی 21 صفحه تعداد کلمات فایل ترجمه شده: 5800 کلمه
چکیده انگلیسی:
In this article, a constitutive formulation of a transversely-isotropic material and failure model for fiber-reinforced polymers is presented comprisin pre-failure material nonlinearities, a novel invariant based quadratic failure criterion (IQC) as well as post failure material softening. The failure surface of the IQ criterion is assumed to take the influence of triaxiality on fracture into account. Further, a distinction between fiber failure and inter-fiber failure is conducted. Material softening is governed by a fracture energy formulation and the introduction of an internal length. The constitutive model is implemented into a programming user interface of the commercial finite element program Abaqus. As results, different laminate lay-ups are modelled and exposed to different stress states in an FE analysis. The obtained failure surfaces and stress strain curves for each laminate lay-up are compared to experimental data. As further applications of the material model presented, a curved composite beam, showing delamination, and a 0°/90°/0°-rod, showing the characteristic damage state in the 90°layer, are simulated and compared.to tests
ترجمه چکیده:
در این مقاله، فرمول سازنده ماده ی ایزوتروپ عرضی و مدل شکست پلیمرهای تقویت شده با الیاف ارائه شده است که شامل غیرخطی بودن پیش از شکست ماده، معیار شکست درجه دوم بر اساس ثوابت (IQC) و نرم شدگی پس از شکست هستند. فرض می شود که سطح شکست در معیار IQ تحت تأثیر سه محوری بودن شکست قرار می گیرد. علاوه بر این، در رابطه با تمایز بین شکست الیاف و شکست بین الیاف نیز بحث خواهد شد. نرم شدن ماده توسط فرمول انرژی شکست و معرفی طول داخلی شرح داده می شود. مدل سازنده در برنامه ی المان محدود آباکوس اجرا می گردد. در نتیجه، لایه های فشرده شده پس از مدلسازی، تحت حالت های تنش مختلف در آنالیز FE قرار می گیرد. سطوح شکست حاصل و منحنی های تنش- کرنش هر لایه با داده های تجربی مقایسه می شود. به عنوان معرفی یکی از کاربردهای مدل پیشنهادی، یک تیر کامپوزیتی خمیده که تحت ورقه ای شدن قرار گرفته و یک میله ی ֯0/ ֯90/ ֯0 که خسارت وارد به آن در لایه ی ֯90 بوده است، شبیه سازی شده و از نظر نتایج تست مقایسه شدند.
فایل انگلیسی شامل 26 صفحه و فایل ترجمه فارسی شامل 21 صفحه است.
تعداد کلمات فایل ترجمه شده: 5800 کلمه
دانلود رایگان مقاله انگلیسی